| View Control |
DM |
|
 |
![View Control[VCF Type]](../images/con_vcf.jpg) |
[VCF Type]
characteristics
Shin-Etsu VC-Film is louver sheet for veiw angle control and visibility
improvement.
VC-Film is constructed of minute black silicone rubber louvers that are
placed in a transparent silicone rubber. Two polycarbonate film is layered
on outer surface. |
|
 |
  |
|
| Chemical Solvent |
Light Transmittance
(Before soaking) |
Light Transmittance
(After soaking) |
Appearance
change |
| Methanol |
78.0% |
78.0% |
None |
| Ethanol |
77.9% |
77.9% |
| Neutral Detergent |
77.8% |
77.7% |
| Leather wax |
77.9% |
78.7% |
| Engine oil |
77.9% |
78.2% |
| Chocolate |
78.0% |
78.1% |
| Regular gasoline |
77.6% |
76.8% |
Slightly swollen
at edge |
| Special gasoline |
77.8% |
76.6% |
|
|
 |
|
|
| Characteristics |
Item |
Characteristic value |
Unit |
Test method |
| Thermal characteristics |
Deflection temperature |
126.8 |
°C |
JIS- K- 7207 |
| Linear expanslon coefficient |
8.0 |
10-5mm/mm/°C |
ASTM- D- 696 |
| Heat shrinkage |
TD 0.15 |
% |
JIS- K- 6735 |
| MD 0.10 |
% |
JIS- K- 6735 |
| Flammability |
SE class |
|
FMVSS- 302 |
| Mechanical characteristics |
Tensile strength |
300 |
kg/cm² |
JIS- K- 7113 |
| Elongation |
110 |
% |
JIS- K- 7113 |
| Peel strength |
1.3 |
kg/25mm |
JIS- K- 6854 |
| Optical characteristics |
Light transmittance |
78 |
% |
JIS- K- 7105 |
|
|
 |
|
|
| Test item |
Test condition |
Peeling |
Color change |
Dimensional Change |
Warp |
| Higt-temperature test |
85°C(1000hrs) |
None |
None |
-0.03 % |
None |
| 120°C(240hrs) |
None |
-0.04 % |
| Low-temperature test |
-40°C(240hrs) |
None |
None |
| Higt-temperature/higt-humidity
test |
60°C,95%RH(240hrs) |
None |
+0.02 % |
| 80°C,95%RH(240hrs) |
None |
-0.02 % |
| Weatherabillity test |
240hrs |
None |
- |
| 480hrs |
Slight color change |
- |
| Thermal shock |
-40°C(1hr)`85°C(1hr)×100cycles |
None |
-0.02 % |
| Heat cycle |
85°C(2hrs)-
Room temperature(2hrs)
-40°C(2hrs)-Room temperature
(2hrs)×20cycles |
6 |
-0.02 % |
|
|
Notes:1.VC 908300 used as a test Samle.
2.Sample size 100×20mm(100mm in the louver axial direction).
3.Warp of the sample,placed on the aluminum place,was measured using a clearance
gauge.
4.The sunshine-type wearher mecer was used for the wearhecability rest with
black panel rempecature of 63 deg.. |
|
 |
|
|
| TYPE |
Visible angle |
Louver angle |
Max. light transmittance angle |
Tickness |
Outer dimension |
| VC- 128500 |
120 ° |
0 ° |
0 ° |
0.9 |
260×300 |
| VC- 128510 |
10 ° |
11 ° |
| VC- 128518 |
18 ° |
23 ° |
| VC- 908500 |
90 ° |
0 ° |
0 ° |
0.9 |
| VC- 908510 |
10 ° |
11 ° |
| VC- 908518 |
18 ° |
23 ° |
| VC- 609500 |
60 ° |
0 ° |
0 ° |
1.0 |
| VC- 609510 |
10 ° |
11 ° |
| VC- 609518 |
18 ° |
23 ° |
|
|
Note)
Every item or numerical value indicated herein is measured by Shine-Etsu
and out of guarantee.
The quality of the connector, which bas been already assmblied, is out of
guarantee.
Please make sure to see about the purpose/conditions of use and practice
your own test.
Industrial ownership like patent doesn't guarantee the usage of the connector. |
| |
|